Data Sheets for Download:
TECANYL®, due to its inherent chemical composition, exhibits unusually low moisture absorption. Therefore, good electrical insulating properties are realized over a wide range of humidity and temperature conditions. Chemical attack from water, most salt solutions, acids and bases is also minimal with TECANYL®. The addition of glass fiber reinforcement enhances both the mechanical and thermal properties of the basic TECANYL® material. Made from Noryl® EN265 resin.
- Good electrical insulating properties
Due to its extremely low water absorption with values as low as 0.07%, TECANYL® is an excellent electrical insulating material.
- Long-term dimensional stability
- Superior impact strength
TECANYL® has a notched Izod impact strength of 3.5 ft-lbs/in.
- TECANYL® exhibits a continuous use temperature in excess of 220°F
- Wide range of UL flammability ratings from
UL94 HB to UL94 V-1
- Light weight
TECANYL®, with a density of 0.0383 lbs/in3, can be used in applications where weight is a significant consideration.
- Thermoformable capability
- Possesses good hydrolytic stability
Made from Noryl EN265 resin® exhibits a broad range of outstanding properties for applications in computers and business equipment, automotive, electrical insulation, telecommunications, appliances, electronics, and many other industries.
|Mechanical||Modulus of elasticity (tensile test)||@ 73°F||350,000||psi||ASTM D 638|
|Tensile strength at break||@ 73°F||9,200||psi||ASTM D 638|
|Elongation at break||@ 73°F||25||%||ASTM D 638|
|Flexural strength||@ 73°F||13,400||psi||ASTM D 790|
|Modulus of elasticity (flexural test)||@ 73°F||370,000||psi||ASTM D 790|
|Impact strength (Izod)||@ 73°F||3.5||ft-lbs/in||ASTM D 256|
|Rockwell hardness||@ 73°F R Scale||119||ASTM D 785|
|Coefficient of friction||Static||0.39||ASTM D 3702|
|Coefficient of friction||Dynamic, 40 psi, 50 fpm||0.32||ASTM D 3702|
|Thermal||Vicat softening point||310||°F||–|
|Deflection temperature||@ 66 psi||279||°F||ASTM D 648|
|Deflection temperature||@ 264 psi||254||°F||ASTM D 648 1)||1) Injection molded sample|
|Service temperature||Long term||220||°F||–|
|Thermal expansion (CLTE)||3.3*105||in/in/°F||ASTM D 696|
|Electrical||Volume resistivity||@ 73°F||1*1017||Ω*cm||ASTM D 257|
|Dielectric strength||500||V/mil||ASTM D 149|
|Dissipation factor||@ 60 Hz, 73°F||0.0007||ASTM D 150 2)||2) Injection molded samples|
|Dielectric constant||@ 60 Hz, 73°F, 50% RH||2.7||ASTM D 150|
|Other||Moisture absorption||@ 24 hours, 73°F||0.07||%||ASTM D 570|
|Flammability (UL94)||V-1||3)||3) thickness greater than 1.5 mm, injection molded samples|
|Flammability (UL94)||V-0||4)||4) thickness greater than 6 mm, injection molded samples|